Исследование процесса тиснения на картонных складных коробках для косметической продукции по (стр. 9 из 11)
| Т, 0С | Н внутр. мкм | Н внеш. мкм | ||||||
| 1 сектор | 2 сектор | 3 сектор | 4 сектор | 1 сектор | 2 сектор | 3 сектор | 4 сектор | |
| 180 | 245,0 | 69,0 | 52,0 | 252,0 | 289,0 | 128,0 | 108,0 | 218,0 |
| 241,0 | 90,0 | 63,0 | 244,0 | 290,0 | 100,0 | 69,0 | 238,0 | |
| Среднее | 243,0 | 79,5 | 57,5 | 248,0 | 289,5 | 114,0 | 88,5 | 228,0 |
| 160 | 162,0 | 81,0 | 54,0 | 215,0 | 197,0 | 67,0 | 48,0 | 150,0 |
| 171,0 | 54,0 | 60,0 | 213,0 | 208,0 | 61,0 | 44,0 | 147,0 | |
| Среднее | 166,5 | 67,5 | 57,0 | 214,0 | 202,5 | 64,0 | 46,0 | 148,5 |
| 140 | 166,0 | 65,0 | 48,0 | 170,0 | 187,0 | 63,0 | 47,0 | 145,0 |
| 161,0 | 49,0 | 52,0 | 147,0 | 184,0 | 62,0 | 41,0 | 131,0 | |
| Среднее | 113,5 | 57,0 | 50,0 | 158,5 | 185,5 | 62,5 | 44,0 | 138,0 |
| 120 | 73,0 | 39,0 | 30,0 | 96,0 | 69,0 | 38,0 | 23,0 | 52,0 |
| 74,0 | 35,0 | 21,0 | 98,0 | 61,0 | 33,0 | 31,0 | 58,0 | |
| Среднее | 73,5 | 37,0 | 25,5 | 97,0 | 65,0 | 35,5 | 27,0 | 55,0 |
Рис. 4.1. График зависимости остаточной деформации от температуры для SUGARLakePaper «Слоновая кость» 310 гр
Таблица 4.19
| «Высоко-белый», Е0 = 0%, Н = 0 мкм | ||||||||
| Т, С | Н внутр., мкм | Н внеш., мкм | ||||||
| 1 сектор | 2 сектор | 3 сектор | 4 сектор | 1 сектор | 2 сектор | 3 сектор | 4 сектор | |
| 180 | 96,0 | 40,0 | 35,0 | 84,0 | 76,0 | 42,0 | 39,0 | 67,0 |
| 123,0 | 47,0 | 30,0 | 91,0 | 67,0 | 47,0 | 34,0 | 55,0 | |
| 94,0 | 46,0 | 39,0 | 79,0 | 83,0 | 47,0 | 36,0 | 68,0 | |
| среднее | 104,3 | 44,3 | 34,7 | 84,7 | 75,3 | 45,3 | 36,3 | 63,3 |
| 160 | 85,0 | 29,0 | 23,0 | 82,0 | 48,0 | 36,0 | 31,0 | 52,0 |
| 73,0 | 29,0 | 21,0 | 77,0 | 58,0 | 33,0 | 31,0 | 53,0 | |
| 71,0 | 34,0 | 25,0 | 77,0 | 51,0 | 46,0 | 31,0 | 57,0 | |
| среднее | 76,3 | 30,7 | 23,0 | 78,7 | 52,3 | 38,3 | 31,0 | 54,0 |
| 140 | 37,0 | 10,0 | 69,0 | 44,0 | 25,0 | 23,0 | 47,0 | |
| 33,0 | 8,0 | 57,0 | 43,0 | 30,0 | 27,0 | 41,0 | ||
| 37,0 | 23,0 | 67,0 | 40,0 | 25,0 | 27,0 | 48,0 | ||
| среднее | 35,7 | 13,7 | 64,3 | 42,3 | 26,7 | 25,7 | 45,3 | |
| 120 | 27,0 | 38,0 | 33,0 | 25,0 | ||||
| 23,0 | 31,0 | 40,0 | 25,0 | |||||
| 27,0 | 43,0 | 37,0 | 28,0 | |||||
| среднее | 25,7 | 37,3 | 36,7 | 26,0 | ||||
| 100 | 25,0 | 17,0 | ||||||
| 20,0 | 20,0 | |||||||
| 33,0 | 31,0 | |||||||
| среднее | 26,0 | 22,7 | ||||||
Рис. 4.2. График зависимости остаточной деформации от температуры для SUGARLakePaper «Высоко-белый» 310 гр
Таблица 4.20
| «Бронза», Е5 = 0,68%, Н = 10,57 мкм | ||||||||
| Т, С | Н внутр., мкм | Н внеш., мкм | ||||||
| 1 сектор | 2 сектор | 3 сектор | 4 сектор | 1 сектор | 2 сектор | 3 сектор | 4 сектор | |
| 180 | 248,0 | 118,0 | 75,0 | 254,0 | 287,0 | 123,0 | 111,0 | 262,0 |
| 201,0 | 120,0 | 77,0 | 266,0 | 316,0 | 156,0 | 118,0 | 277,0 | |
| среднее | 224,5 | 119,0 | 76,0 | 260,0 | 301,5 | 139,5 | 114,5 | 269,5 |
| 160 | 122,0 | 76,0 | 82,0 | 108,0 | 194,0 | 103,0 | 86,0 | 155,0 |
| 138,0 | 66,0 | 76,0 | 101,0 | 176,0 | 138,0 | 96,0 | 157,0 | |
| среднее | 130,0 | 71,0 | 79,0 | 104,5 | 185,0 | 120,5 | 91,0 | 156,0 |
| 140 | 163,0 | 64,0 | 59,0 | 105,0 | 181,0 | 117,0 | 80,0 | 161,0 |
| 88,0 | 54,0 | 37,0 | 100,0 | 172,0 | 94,0 | 67,0 | 144,0 | |
| среднее | 125,5 | 59,0 | 48,0 | 102,5 | 176,5 | 105,5 | 73,5 | 152,5 |
| 120 | 120,0 | 57,0 | 46,0 | 92,0 | 150,0 | 100,0 | 71,0 | 146,0 |
| 90,0 | 81,0 | 150,0 | 94,0 | 69,0 | 139,0 | |||
| среднее | 105,0 | 57,0 | 46,0 | 86,5 | 150,0 | 97,0 | 70,0 | 142,5 |
Рис. 4.3. График зависимости остаточной деформации от температуры для РЕГЕНТ Маджестик «Бронза» (двухсторонний) 250 гр
Таблица 4.21
| «Золото», Е0 = 0%, Н = =0 мкм | ||||||||
| Т, С | Н внутр., мкм | Н внеш., мкм | ||||||
| 1 сектор | 2 сектор | 3 сектор | 4 сектор | 1 сектор | 2 сектор | 3 сектор | 4 сектор | |
| 180 | 71,0 | 63,0 | 48,0 | 27,0 | 75,0 | |||
| 65,0 | 68,0 | 48,0 | 35,0 | 90,0 | ||||
| 65,0 | 37,0 | 37,0 | 94,0 | |||||
| среднее | 68,0 | 65,3 | 44,3 | 33,0 | 86,3 | |||
| 160 | 50,0 | 28,0 | 20,0 | 63,0 | 85,0 | 35,0 | 24,0 | 78,0 |
| 53,0 | 21,0 | 63,0 | 84,0 | 31,0 | 28,0 | 81,0 | ||
| 48,0 | 22,0 | 65,0 | 75,0 | 29,0 | 27,0 | 78,0 | ||
| среднее | 50,3 | 28,0 | 21,0 | 63,7 | 81,3 | 31,7 | 26,3 | 79,0 |
| 140 | 31,0 | 23,0 | 67,0 | 17,0 | 10,0 | 42,0 | ||
| 30,0 | 38,0 | 66,0 | 19,0 | 15,0 | 39,0 | |||
| 30,0 | 41,0 | 62,0 | 20,0 | 14,0 | 64,0 | |||
| среднее | 30,3 | 34,0 | 65,0 | 18,7 | 13,0 | 48,3 | ||
| 120 | 18,0 | 34,0 | 15,0 | 33,0 | ||||
| 16,0 | 32,0 | 12,0 | 42,0 | |||||
| 13,0 | 29,0 | 14,0 | 34,0 | |||||
| среднее | 15,7 | 31,7 | 13,7 | 36,3 | ||||
| 100 | 26,0 | 17,0 | ||||||
| 27,0 | 15,0 | |||||||
| 28,0 | 16,0 | |||||||
| среднее | 27,0 | 16,0 | ||||||
Рис. 4.4. График зависимости остаточной деформации от температуры для РЕГЕНТ Curiousmetallic «Золото» 270 гр
Таблица 4.22. Дизайнерский картон SUGARLakePaper «Слоновая кость» 310 гр и фольга CrownRollLeafIncYED (черная)
| Е1 = 0%, Н = 0 мкм | ||||||||
| t C | Чёткость тиснения, балл | Укрывистость, балл | ||||||
| 1 | 2 | 3 | Ср. | 1 | 2 | 3 | Ср. | |
| 100 | 0,00 | 0,25 | 0,25 | 0,17 | 0,8 | 0,4 | 0,3 | 0,5 |
| 120 | 0,00 | 0,25 | 0,25 | 0,17 | 2,0 | 1,1 | 1,5 | 1,5 |
| 140 | 0,25 | 0,00 | 0,00 | 0,08 | 6,2 | 5,8 | 6,7 | 6,2 |
| 160 | 0,25 | 0,00 | 0,00 | 0,08 | 12,8 | 12,1 | 11,6 | 12,2 |
| 180 | 0,25 | 0,25 | 0,00 | 0,17 | 6,6 | 8,7 | 7,3 | 7,5 |
Таблица 4.23
| Е3 = 0,35%, Н = 5,48 мкм | |||||||||
| t C | Чёткость тиснения, балл | Укрывистость, балл | Прочность к истиранию, цикл | ||||||
| 1 | 2 | Ср. | 1 | 2 | Ср. | 1 | 2 | Ср. | |
| 100 | 1,00 | 0,75 | 0,88 | 7,2 | 5,5 | 6,4 | |||
| 120 | 1,25 | 1,00 | 1,13 | 15,1 | 13,9 | 14,5 | |||
| 140 | 1,00 | 0,50 | 0,75 | 21,3 | 18,8 | 20,1 | 90 | 87 | 89 |
| 160 | 0,25 | 0,00 | 0,13 | 42,5 | 41,3 | 41,9 | 118 | 110 | 115 |
Таблица 4.24
| Е4 = 0,525%, Н = 8,22 мкм | |||||||||
| t C | Чёткость тиснения, балл | Укрывистость, балл | Прочность к истиранию, цикл | ||||||
| 1 | 2 | Ср. | 1 | 2 | Ср. | 1 | 2 | Ср. | |
| 100 | 1,00 | 2,00 | 1,50 | 11,2 | 10,9 | 11,1 | |||
| 120 | 0,25 | 0,25 | 0,25 | 17,4 | 16,4 | 16,9 | |||
| 140 | 0,25 | 0,00 | 0,13 | 38,7 | 36,1 | 37,4 | 138 | 140 | 139 |
| 160 | 1,75 | 2,00 | 1,88 | 48,6 | 47,7 | 48,2 | 182 | 194 | 188 |
| 180 | 0,25 | 0,50 | 0,38 | 69,8 | 67,4 | 68,6 | 172 | 165 | 169 |
Таблица 4.25
| Е5 = 0,700%, Н = 10,95 мкм | |||||||||
| t C | Чёткость тиснения, балл | Укрывистость, балл | Прочность к истиранию | ||||||
| 1 | 2 | Ср. | 1 | 2 | Ср. | 1 | 2 | Ср. | |
| 100 | 0,25 | 0,25 | 0,25 | 37,4 | 38,9 | 38,2 | 211 | 223 | 217 |
| 120 | 0,25 | 0,25 | 0,25 | 26,1 | 24,6 | 25,4 | 254 | 260 | 257 |
| 140 | 1,00 | 1,00 | 1,00 | 71,2 | 72,7 | 72,0 | 390 | 398 | 394 |
| 160 | 3,00 | 2,00 | 2,50 | 74,6 | 81,2 | 77,9 | 418 | 410 | 414 |
| 180 | 0,75 | 0,50 | 0,63 | 27,3 | 26,5 | 26,9 | 273 | 281 | 277 |
Рис. 4.5. График зависимости укрывистости оттиска от температуры
Рис. 4.6. График зависимости прочности к истиранию от деформации
Таблица 4.26. Дизайнерский картон SUGARLakePaper «Белое золото» 250 гр. и фольгаKURZ Colorit V 963 (красная)
| Е1 = 0%, Н = 0 мкм | ||||||||
| t C | Чёткость тиснения, балл | Укрывистость, балл | ||||||
| 1 | 2 | 3 | Ср. | 1 | 2 | 3 | Ср. | |
| 100 | 0,25 | 0,25 | 0,50 | 0,3 | 1,0 | 1,4 | 1,5 | 1,3 |
| 110 | 0,25 | 0,25 | 0,25 | 0,3 | 1,5 | 1,6 | 1,6 | 1,6 |
| 120 | 0,50 | 0,00 | 0,25 | 0,3 | 1,7 | 1,7 | 1,6 | 1,7 |
| 130 | 0,25 | 0,00 | 0,00 | 0,1 | 1,8 | 2,0 | 1,7 | 1,8 |
| 140 | 0,00 | 0,00 | 0,00 | 0,0 | 1,7 | 2,0 | 1,7 | 1,8 |
Таблица 4.27